Addressing H-Material Interaction in Fast Diffusion Materials—A Feasibility Study on a Complex Phase Steel


Hydrogen embrittlement (HE) is one of the main limitations in the use of advanced high-strength steels in the automotive industry. To have a better understanding of the interaction between hydrogen (H) and a complex phase steel, an in-situ method with plasma charging was applied in order to provide continuous H supply during mechanical testing in order to avoid H outgassing. For such fast-H diffusion materials, only direct observation during in-situ charging allows for addressing H effects on materials. Different plasma charging conditions were analysed, yet there was not a pronounced effect on the mechanical properties. The H concentration was calculated while using a simple analytical model as well as a simulation approach, resulting in consistent low H values, below the critical concentration to produce embrittlement. However, the dimple size decreased in the presence of H and, with increasing charging time, the crack propagation rate increased. The rate dependence of flow properties of the material was also investigated, proving that the material has no strain rate sensitivity, which confirmed that the crack propagation rate increased due to H effects. Even though the H concentration was low in the experiments that are presented here, different technological alternatives can be implemented in order to increase the maximum solute concentration.

Funding source: COMET program, K2 Center “Integrated Computational Material, Process and Product Engineering (IC-MPPE)” (Project No 859480); Austrian Federal Ministries for Climate Action, Environment, Energy, Mobility, Innovation and Technology (BMK) ; Digital and Economic Affairs (BMDW); Austrian research funding association (FFG); federal states of Styria, Upper Austria and Tyrol.
Countries: Austria ; Germany

Article metrics loading...

This is a required field
Please enter a valid email address
Approval was a Success
Invalid data
An Error Occurred
Approval was partially successful, following selected items could not be processed due to error